供应沙伯基础 Xenoy 6380U PBT+PET 抗紫外线
SABIC Innovative Plastics Xenoy® 6380U PBT+PET (Asia Pacific)物性表
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.51 g/cc | 1.51 g/cc | ASTM D 792 |
密度 | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
平衡吸湿 | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
饱和吸水率 | 0.50 % @Temperature 23.0 °C | 0.50 % @Temperature 73.4 °F | ISO 62 |
线性成型收缩率,Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | on tensile bar; SABIC Method |
0.0030 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0070 in/in @Thickness 0.126 in | SABIC Method | |
熔体流动速率 | 9.0 g/10 min @Load 1.20 kg, Temperature 265 °C | 9.0 g/10 min @Load 2.65 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
13 g/10 min @Load 1.20 kg, Temperature 266 °C | 13 g/10 min @Load 2.65 lb, Temperature 511 °F | ASTM D 1238 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
洛氏硬度(R 级) | 110 | 110 | ISO 2039-2 |
硬度,H358/30 | 115 MPa | 16700 psi | ISO 2039-1 |
抗张强度(断裂) | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D 638 |
105 MPa | 15200 psi | 5 mm/min; ISO 527 | |
抗张强度(屈服) | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D 638 |
105 MPa | 15200 psi | 5 mm/min; ISO 527 | |
伸长率 (断裂) | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
屈服伸长率 | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
拉伸模量 | 8.20 GPa | 1190 ksi | 5 mm/min; ASTM D 638 |
8.40 GPa | 1220 ksi | 1 mm/min; ISO 527 | |
弯曲强度 | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
弯曲模量 | 7.00 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 | |
悬壁梁缺口冲击强度 | 0.600 J/cm @Temperature -30.0 °C | 1.12 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
Izod Impact, Unnotched | 6.00 J/cm @Temperature -30.0 °C | 11.2 ft-lb/in @Temperature -22.0 °F | ASTM D 4812 |
6.50 J/cm @Temperature 23.0 °C | 12.2 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 | |
悬壁梁缺口冲击强度 | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
10.0 kJ/m² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
悬壁梁无缺口冲击强度 | 40.0 kJ/m² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U |
40.0 kJ/m² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U | |
简支梁无缺口冲击强度 | 3.50 J/cm² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
4.00 J/cm² @Temperature 23.0 °C | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
简支梁缺口冲击强度 | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
1.00 J/cm² @Temperature 23.0 °C | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
冲击试验 | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
体积电阻率 | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
介电常数 | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | IEC 60250 |
4.2 @Frequency 50.0 - 60.0 Hz | 4.2 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
介电强度 | 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
20.0 kV/mm @Thickness 1.60 mm | 508 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
耗散因数 | 0.0020 @Frequency 50.0 - 60.0 Hz | 0.0020 @Frequency 50.0 - 60.0 Hz | IEC 60250 |
0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |
相比耐漏电起痕指数(CTI) | 300 V | 300 V | IEC 60112 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线形热膨胀系数 - 流动 | 23.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 12.8 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
25.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 13.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
线性热膨胀系数,横向流动 | 100 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
130 µm/m-°C @Temperature 23.0 - 80.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
导热系数 | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ISO 8302 |
载荷下热变形温度(0.46 MPa) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
载荷下热变形温度(1.8 MPa) | 180 °C | 356 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
165 °C @Thickness 3.20 mm | 329 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
维卡软化温度 | 180 °C | 356 °F | Rate B/120; ISO 306 |
180 °C | 356 °F | Rate B/50; ISO 306 | |
180 °C | 356 °F | Rate B/50; ASTM D 1525 | |
215 °C | 419 °F | Rate A/50; ISO 306 | |
可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 |
HB @Thickness 3.00 mm | HB @Thickness 0.118 in | 2nd value; UL 94 | |
灼热丝试验 | 750 °C @Thickness 3.20 mm | 1380 °F @Thickness 0.126 in | Glow Wire Flammability Index; IEC 60695-2-12 |
材料描述 | 测试方法 | |
---|---|---|
Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |