桥梁主梁用美标工字钢型号规格对照
| 美标工字钢型号 | G | h | b | tw | tf |
| kg/m | mm | mm | mm | mm | |
| S 3 x 5.7 | 8.5 | 76 | 59 | 4.3 | 6.6 |
| S 3 x 7.5 | 11.2 | 76 | 64 | 8.9 | 6.6 |
| S 4 x 7.7 | 11.5 | 102 | 68 | 4.9 | 7.4 |
| S 4 x 9.5 | 14.1 | 102 | 71 | 8.3 | 7.4 |
| S 5 x 10 | 15.0 | 127 | 76 | 5.4 | 8.3 |
| S 6 x 12.5 | 18.6 | 152 | 85 | 5.9 | 9.1 |
| S 6 x 17.25 | 25.7 | 152 | 91 | 11.8 | 9.1 |
| S 8 x 18.4 | 27.4 | 203 | 102 | 6.9 | 10.8 |
| S 8 x 23 | 34.0 | 203 | 106 | 11.2 | 10.8 |
| S 10 x 25.4 | 37.8 | 254 | 118 | 7.9 | 12.5 |
| S 10 x 35 | 52.0 | 254 | 126 | 15.1 | 12.5 |
| S 12 x 31.8 | 47.3 | 305 | 127 | 8.9 | 13.8 |
| S 12 x 35 | 52.0 | 305 | 129 | 10.9 | 13.8 |
| S 12 x 40.8 | 60.7 | 305 | 133 | 11.7 | 16.7 |
| S 12 x 50 | 74.0 | 305 | 139 | 17.4 | 16.7 |
| S 15 x 42.9 | 64.0 | 381 | 140 | 10.4 | 15.8 |
| S 15 x 50 | 74.0 | 381 | 143 | 14 | 15.8 |
| S 18 x 54.7 | 81.4 | 457 | 152 | 11.7 | 17.6 |
| S 18 x 70 | 104 | 457 | 159 | 18.1 | 17.6 |
| S 20 x 66 | 98.0 | 508 | 159 | 12.8 | 20.2 |
| S 20 x 75 | 112 | 508 | 162 | 16.1 | 20.2 |
| S 20 x 86 | 128 | 515.62 | 179 | 16.8 | 23.4 |
| S 20 x 96 | 143 | 515.62 | 183 | 20.3 | 23.4 |
| S 24 x 80 | 119 | 609.6 | 178 | 12.7 | 22.1 |
| S 24 x 90 | 134 | 609.6 | 181 | 15.9 | 22.1 |
| S 24 x 100 | 149 | 609.6 | 184 | 18.9 | 22.1 |
| S 24 x 106 | 158 | 622.3 | 200 | 15.7 | 27.7 |
| S 24 x 121 | 180 | 622.3 | 204 | 20.3 | 27.7 |