ASA韩国LGLI931
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 1.07 | g/cm3 | |
| 熔流率（熔体流动速率）(220°C/10.0kg) | ASTMD1238 | 7.0 | g/10min | ||
| 收缩率-流动(3.20mm) | ASTMD955 | 0.40to0.70 | % | ||
| 机械性能 | 抗张强度2(屈服,3.20mm) | ASTMD638 | 32.4 | MPa | |
| 伸长率2(断裂,3.20mm) | ASTMD638 | 65 | % | ||
| 弯曲模量3(6.40mm) | ASTMD790 | 1520 | MPa | ||
| FlexuralStrength3(6.40mm) | ASTMD790 | 49.0 | MPa | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | -30°C,3.20mm | ASTMD256 | 49 | J/m |
| -30°C,6.40mm | ASTMD256 | 39 | J/m | ||
| 23°C,3.20mm | ASTMD256 | 98 | J/m | ||
| 23°C,6.40mm | ASTMD256 | 88 | J/m | ||
| 硬度 | 洛氏硬度(R级) | ASTMD785 | 81 | ||
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,6.40mm) | ASTMD648 | 85.0 | °C | |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | ASTMD648 | 79.0 | °C | ||
| 维卡软化温度 | ASTMD15254 | 86.0 | °C | ||
| 光学性能 | 光泽度(45°) | ASTMD2457 | 30 | ||