锻打过程中，对于冲孔工序，应尽量采用小头冲孔，后扩孔。初冲孔直径为公称孔径的1／2.5—1／3，冲孔前端面平整，用初冲头的中心压印，上煤末后再冲孔，尽量采用双面冲孔，
防止下端面出现毛刺。法兰锻打过程要勤卡勤量并严格掌握控制好锻造温度在规定的范围内。
(3)选择适当的锻造比，一般情况下选用≥2，锻锤的吨位选择比普通钢大1／3，克服热状态下的高变形抗力，以锻透细化晶粒。
(4)法兰锻后采用空冷，使锻件冷和变形时析出的碳化物完全溶解到奥氏体中去，提高抗腐蚀能力，并进行固溶处理。
超级不锈钢、双相不锈钢、镍基合金钢
黑皮棒、光亮棒、抛光棒、磨光棒、六角棒、棒料、棒材、研磨棒
锻环、方块锻件、锻件、锻圆、锻饼、异形锻件
1、超级不锈钢
904L/N08904/1.4539/00Cr20Ni25Mo4.5Cu/015Cr21Ni26Mo5Cu2
Incoloy926/N08926/1.4529/Mo6CuN/Incoloy alloy25-6Mo、
AL-6XN/N08367/1.4501/00Cr21Ni24MoN/Incoloy alloy25-6HN/NAS 255NM、
254SMO/S31254/1.4547/F44/00Cr21Ni25Mo6CuN/015Cr20Ni18Mo6CuN、
654SMo/S32654/1.4652/00Cr24Ni22Mo7Mn3CuN、
Incoloy840/S33400/NAS H840、
253MA/S30815/1.4835/F45、
310/S31000/20Cr25Ni20/S31020
310S/S31008/06Cr25Ni20
314/S31400/16Cr25Ni20Si2/S38340
304L/S30403/022Cr19Ni10/S30403/
304LN/S30453/022Cr19Ni10N/S30453
316/S31600/06Cr17Ni12Mo2/S31608
316L/S31603/022Cr17Ni12Mo2/S31603
316LN/S31653/022Cr17Ni12Mo2N/S31653
316Ti/S31635/06Cr17Ni12Mo2Ti/S31668
317/S31700/06Cr19Ni13Mo3
317L/S31703/022Cr19Ni13Mo3/S31703
317LN/S31753/022Cr19Ni13Mo4N/S31753
317LMN/S31726/022Cr19Ni16Mo5N/S31726
321/S32100/06Cr18Ni11Ti/S32168
347/S34700/06Cr18Ni11Nb/S34778
384/S38400/06Cr18Ni18/S30608
Nitronic50/XM-19/Fxm-19/S20910/00Cr22Ni13Mn5Mo2N、
Nitronic60/S21800/0Cr17Ni9Mn8Si4N
724L/316Lmod
725LN/310MoLN/S31050/022Cr25Ni22Mo2N/S31053/25-22-2
2、沉淀硬化钢：
17-4PH/630/S17400/1.4542/05Cr17Ni4Cu4Nb/S51740
17-7PH/631/S17700/1.4568/07Cr17Ni7Al/S51700
15-5PH/XM-12/S15500/1.4545/05Cr15Ni5Cu4Nb、
15-7MoPH/632/S15700/1.4532/07Cr15Ni7Mo2AL/S51570
3、双相不锈钢
2205/S31803/F51/1.4462/022Cr22Ni5Mo3N/S22253、
2205/S32205/F60/022Cr23Ni5Mo3N/S22053
2507/S32750/F53/1.4410/022Cr25Ni7Mo4N/S25073
255/S32550/F61/1.4507/329J2L/03Cr25Ni6Mo3Cu2N/S25554
Zeron100/S32760/F55/1.4501/022Cr25Ni7Mo4WCuN/S27603
2304/S32304/1.4362/022Cr23Ni4MoCuN/S23043
3RE60/S31500/1.4424/022Cr18Ni5Mo3Si2N/S21953
329/S32900/1.4460/F52/06Cr26Ni4Mo2/S22693
2101/S32101/1.4162/00Cr21Mn5Ni1.5N
DP3/S31260/022Cr25Ni7Mo3WCuN/S22583
4、纯镍
Nickel200/N02200/2.4060/N6（6号镍）、
Nickel201/N02201/2.4060/N4（4号镍）
5、蒙乃尔合金钢
Monel400/N04400/2.4360、MonelK500/N05500/2.4375/Monel K500
6、哈氏合金钢
Hastelloy C/HC/N10002/2.4819/NS333/NS3303/H03303
Hastelloy C-276/HC-276/N10276/2.4819/NS334/NS3304/H03304
Hastelloy C-4/HC-4/N06455/2.4610/NS335/NS3305/H03305
Hastelloy C-22/HC-22/Inconel622/N06022/2.4602/NS3308/H03308
Hastelloy C-59/
Hastelloy C-2000/HC-2000/N06200/2.4675/NS3405/H03045
Hastelloy B/HB/N10001/2.4800/NS321/NS3201/H03201
Hastelloy B-2/HB-2/N10665/2.4617/NS3203/H03203
Hastelloy B-3/HB-3/N10675/2.4600/NS3203/H03203
Hastelloy B-4/HB-4/N10629/NS3204/H03204
Hastelloy G/N06007/2.4618/NS3402/H03402、
Hastelloy G-3/HG-3/N06985/2.4619/NS3403/H03403
Hastelloy G-30/HG-30/N06030/2.4603/NS3404/H03404
Hastelloy G-35/HG-35
Hastelloy G-50/HG-50/N06950/NS3310/H03310
HastelloyN
7、因科乃尔合金钢
Inconel600/N06600/2.4816/NS312/NS3102/H03102/GH600/GH3600/H36000
Inconel601/N06601/2.4851/NS313/NS3103/H03103
Inconel617/N07617/2.4663
Inconel625/N06625/2.4856/NS336/NS3306/H03306/GH625/GH3625/GH36250
Inconel686/N06686/2.4606/NS3309/H03309
Inconel690/N06690/NS315/NS3105/H03105、
Inconel725/N07725、
8、因科罗伊合金钢
Incoloy800/N08800/1.4876/NS111/NS1101/H01101
Incoloy800H/N08810/1.4876/NS112/NS1102/H01102
Incoloy800HT/N08811/1.4954/NS113/NS1103/H01103
Incoloy825/N08825/2.4858/NS142/NS1402/H01402
Incoloy901/N09901/1.4898
Incoloy925/N09925、
9、高温合金钢
GH2132/GH132/Incoloy A286/N66286/1.4980/H21320
GH2136/GH136/V57/1.4606/H21360
GH3030/GH30/Nimonic 75/N06075/H30300
GH3128/GH128/N06219/2.4855/H31280
GH4145/GH415/Inconel X-750/N07750/2.4469/H41450
GH4169/GH169/Inconel718/N07718/2.4668/H41690
GH4180A/GH80A/Nimonic 80A/N07080/2.4952/H40801
GH3536/GH536/HastelloyX/N06002/2.4613
10、精密合金钢
4J36/Invar36/K93600/1.3912/因瓦(INVAR)合金
4J29/F15/1.3981/可伐(Kovar)合金
1J50、
1J79
3J53
11、特殊钢
Alloy31/N08031/1.4562/NS1404
Alloy33/N08033/1.4591/NS1405
Alloy20/Alloy20Cb-3/Carpenter20Cb-3/N08020/2.4660/NS143/NS1403/H01403/GH15/GH1015/H10150
二、规格范围
各种标准或非标锻件,按客户需要或图纸订做;
三、执行标准
ASTM 182、GB1220、B564、B637、B462
四、可提供的品种
锻环、方块锻件、锻件、锻圆、锻饼、异性锻件、
五、产地：
宝钢、太钢、汉彻金属、美国、瑞典、欧美进口
(1)生产车间按工艺要求选择法兰合适的原材料下料，加热前必须检查材料的表面，若存在可见的裂缝、折叠、夹杂等缺陷，必须用剥去外皮或其他铲除方法清除干净才允许进炉加热。
(2)锻打采取先以较小变形量进行轻打，待塑性提高后重击原则。并以方形一多角形一方形的方式进行锻打。法兰锻打过程中发现表面存在裂纹或其它缺陷应及时上报质检员和工艺员，进行合理的清除和处理。
镦粗时先把上下端部倒角或圆周压边，再放平贴上重击，法兰毛坯应围绕其轴心线不断转动使均匀变形。毛坯截面大时，可用“压铁”展平镦粗。