ASTM D-792模缩率 (流向1.6mm)-0.1%ASTM D-955泰伯摩擦63mgASTM D-1044模缩率
ASTM D-955 (流向3.2mm)0%
(横向1.6mm)0.9%上海韬盛塑化科技有限公司机械性能额定值单位测试方法弯曲模量(23℃,1.6mm)14000MPaASTM D-790无缺口冲击强度 (23℃,3.2mm)555,20%NBj/mASTMD-4812弯曲模量 (23℃,0.8mm)18000MPaASTM D-790冲击下机械性能210ºCUL 746B拉伸模量(23℃,3.2mm)18000MPaASTM D-638弯曲模量 (23℃,3.2mm)13100MPaASTMD-790 拉伸强度 (23℃,1.6mm)173MPaASTM D-638IZOD冲击强度(23℃,0.8mm)400,40%NBj/mASTM D-256无缺口冲击强度 (23℃,1.6mm)840j/mASTMD-4812模缩率 (横向3.2mm)0.8%ASTM D-955弯曲强度
ASTM D-790 (23℃,3.2mm)183MPa
(23℃,0.8mm)215MPa
压缩强度 (3.2mm)89MPaASTM D-695拉伸模量 (23℃,1.6mm)19306MPaASTM D-638断裂伸长率(23℃,3.2mm)1.7%ASTM D-638弯曲疲劳 (3.2mm.69MPa)2667cycleASTM D-671断裂伸长率(23℃,1.6mm)1.6%ASTM D-638IZOD冲击强度 (23℃,3.2mm)225j/mASTM D-256洛氏硬度(Scale M)63
ASTM D-785拉伸强度 (23℃,3.2mm)150MPaASTM D-638弯曲强度(23℃,1.6mm)192MPaASTM D-790IZOD冲击强度 (23℃,1.6mm)170j/mASTMD-256电气性能额定值单位测试方法介电强度 (1.6mm逐步)31KV/mmASTM D-149介电常数
(23℃,0.8mm,1×10Hz)4.4
ASTM D-2520B (23℃,3.2mm,1×10Hz)4.3
ASTM D-150损耗因素
(23℃,1.6mm,1×10Hz)0.004
ASTM D-2520B (23℃,3.2mm,1×10Hz)0.029
ASTM D-150 (23℃,3.2mm,1×10Hz)0.004
ASTM D-2520B介电强度
ASTMD-149 (23℃,1.6mm短时间)35KV/mm上海韬盛塑化科技有限公司 (23℃,3.2mm短时间)＞28KV/mm
介电常数 (23℃,3.2mm,1×10Hz)3.8
ASTM D-150体积电阻率1×10Ω.cmASTM D-257损耗因素 (23℃,3.2mm,1×10Hz)0.013
ASTM D-150介电常数
(23℃,3.2mm,1×10Hz)4.3
ASTM D-2520B (23℃,0.8mm,1×10Hz)3.9
ASTM D-150损耗因素
ASTM D-150 (23℃,0.8mm,1×10Hz)0.013
(23℃,0.8mm,1×10Hz)0.029
(23℃,0.8mm,1×10Hz)0.004
表面电阻率1×10ΩASTM D-257介电常数 (23℃,0.8mm,1×10Hz)3.5
ASTM D-150加工性能额定值单位测试方法熔解温度范围 (℃)363-371
上海韬盛塑化科技有限公司模具温度范围 (℃)30-95
干燥时间(除湿干燥剂)2h
加工时水气含量＜0.01%
干燥温度135℃
热性能额定值单位测试方法熔点352ºCASTM D-3418导热性0.32W/m kASTM C-177玻璃转变温度120ºCASTMD-3418热变形温度289ºCASTM D-648相关温度指数240ºCUL 746B外推Zui终融温360ºCASTMD-3418其它性能额定值单位测试方法 厚度测试0.75mmUL 94厚度比率V-0
UL 94限制氧气指数 (3.2mm)39%ASTM D-2863
上海韬盛塑化科技有限公司