LUPOY PC 1303-07 resin is designed for extrusion and injectionmolding products. It exhibits an excellent physical propertybalance of heat resistance, transparency and impact strength.
Lupoy® 1303-07 物性表
紫外线稳定剂
特性抗撞击性,良好
耐热性,高
清晰度,高
脱模性能良好
粘度,高
用途薄膜
电器用具
镜头
片材
UL文件号E306922
加工方法挤出
注射成型
物理性能额定值单位制测试方法比重1.20g/cm3ASTM D792熔流率(熔体流动速率) (300°C/1.2 kg)7.0g/10 minASTM D1238收缩率 - 流动0.50 到0.70%ASTM D955吸水率ASTM D570 23°C, 24hr0.15%ASTM D570 平衡, 23°C, 50% RH0.32%ASTM D570硬度额定值单位制测试方法洛氏硬度
ASTM D785 M级74
ASTM D785 R级118
ASTM D785机械性能额定值单位制测试方法拉伸模量2410MPaASTM D638抗张强度
ASTM D638 屈服60.0MPaASTMD638 断裂72.0MPaASTM D638伸长率
ASTM D638 屈服6.0%ASTMD638 断裂150%ASTMD638弯曲模量2410MPaASTM D790弯曲强度96.0MPaASTM D790耐磨耗性 - Change inHaze 145%ASTM D1004可燃性额定值单位制测试方法平均燃烧程度3cmASTMD635冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 2(23°C, 3.20 mm)900J/mASTMD256无缺口悬臂梁冲击 (23°C)无断裂
ASTM D256装有测量仪表的落镖冲击 3(23°C, 3.20 mm, Total Energy)90.0JASTMD3763热性能额定值单位制测试方法载荷下热变形温度
ASTM D648 0.45 MPa,退火, 4.00 mm145°CASTMD648 1.8 MPa, 未退火,4.00 mm129°CASTM D648 1.8 MPa, 退火, 4.00 mm142°CASTM D648维卡软化温度151°CASTMD1525 4球压温度> 125°CIEC 60598-1线形热膨胀系数 -流动 (-40 到 82°C)6.8E-5cm/cm/°CASTMD696电气性能额定值单位制测试方法体积电阻率 (23°C)2.0E+17ohms·cmASTM D257介电强度17kV/mmASTMD149介电常数 (60 Hz)3.00
ASTM D150耗散因数 (60 Hz)1.0E-3
ASTM D150漏电起痕指数 (2.00 mm)250VIEC60112可燃性额定值单位制测试方法UL 阻燃等级
UL 94 0.500mmHB
UL 94 3.00mmHB
UL 94热灯丝点火温度 5(2.00mm)850°CIEC 60695-2-13极限氧指数26%ASTMD2863光学性能额定值单位制测试方法折射率1.586
ASTM D542透射率89.0%ASTM D1003雾度0.70 到 1.5%ASTM D1003备注1 .1000g, 500cycles, CS-10F Wheel2 .0.25 mm 缺口深度3 .3.38 m/sec4 .速率 A (50°C/h),载荷2 (50N)5 .5 sec工艺过程
聚碳酸酯纺织纱管的生产,选用*法生产的PC为原料,其中新料为80%,再生料为20%。其生产工艺流程如下:
配料→干燥→注射→修整→抛光→热处理→制品。
烘箱干燥温度115—120℃, 16-20小时,物料在料盘上厚度为30毫米以下,使树脂含水量在0.03%以下。
料筒三区温度为200—220、 250—280、 260—290℃,喷咀温度比料筒稍低些,低5-10℃。注射压力60—100MPa,成型周期25秒,热处理温度115—120℃, 1小时,要采用倒悬式进行热处理。
该纱管比木质纱管使用寿命长3倍、尺寸稳定、耐候性好,不起毛、光洁度好,能提供各种颜色的纱管,便于搞好班组经济核算。
PC 韩国LG 1303-07PC 韩国LG 1303-07PC 韩国LG 1303-07