| 基本性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 吸水率 (24小时 23℃) | 1.3 | % | ASTM D-570 |
| 比重 | 1.25 | ASTM D-792 |
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 强化含量 | 15 | WT% | |
| 抗燃级 | HB | 1/16") | UL94 |
| 泰伯磨耗量 ((1000g,CS-17)23℃) | 10 | mg/1000次 | ASTM D-1044 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 压缩强度 (80℃) | 700 | kg/cm | ASTM D-695 |
| 抗拉屈股强度 (-40℃) | 1400 | kg/cm | ASTM D-638 |
| 挠曲模量 (23℃) | 51000 | kg/cm | ASTM D-790 |
| 埃佐德衡击 (23℃ 无缺口1/8) | 30 | kg·cm/cm | |
| 挠曲模量 (80℃) | 21000 | kg/cm | ASTM D-790 |
| 裂断伸长率 | ASTM D-638 | ||
| (80℃) | 9 | % | |
| (-40℃) | 3.5 | % | |
| 埃佐德衡击 (23℃ V-缺口1/2) | 5 | kg·cm/cm | ASTM D-256 |
| 挠曲强度 (80℃) | 700 | kg/cm | ASTM D-790 |
| 埃佐德衡击 (-40℃ V-缺口1/2) | 4.5 | kg·cm/cm | ASTM D-256 |
| 洛氏硬度 (M-标度 23℃) | 90 | ASTM D-785 | |
| 挠曲模量 (-40℃) | 68000 | kg/cm | ASTM D-790 |
| 压缩强度 (-40℃) | 2050 | kg/cm | ASTM D-695 |
| 埃佐德衡击 (-40℃ 无缺口1/8) | 19 | kg·cm/cm | |
| 抗拉屈股强度 | ASTM D-638 | ||
| (23℃) | 1050 | kg/cm | |
| (80℃) | 450 | kg/cm | |
| 裂断伸长率 (23℃) | 4 | % | ASTM D-638 |
| 洛氏硬度 (R-标度 23℃) | 119 | ASTM D-785 | |
| 挠曲强度 | ASTM D-790 | ||
| (-40℃) | 1800 | kg/cm | |
| (23℃) | 1500 | kg/cm | |
| 压缩强度 (23℃) | 1400 | kg/cm | ASTM D-695 |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 10 | Ω·cm | ASTM D-257 |
| 介电强度 (短时间 1/8") | 20 | KV/mm | ASTM D-149 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热挠曲温度 | ASTM D-648 | ||
| (18.6kg/cm) | 175 | ℃ | |
| (4.6kg/cm) | 210 | ℃ | |
| 线性热膨胀系数 | 4.5 | ×10-5cm/cm/℃ | ASTM D-696 |
| 熔点 | 225 | ℃ | 差示扫描测热计DSC |
| 比热 | 0.37 | Cal/g·℃ |