| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 比重 | 1.15 | ASTM D-792 | |
| 成型收缩率 | 0.3-0.5 | % | ASTM D-955 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| IZOD缺口冲击强度 | 1.5 | ft.lb/in | ASTM D-256 |
| 拉伸屈服强度 | 78 | MPa | ASTM D-638 |
| 断裂伸长率 | 8 | % | ASTM D-638 |
| 弯曲模量 | |||
| 50000 | Kg/cm | ASTM D-790 | |
| 4900 | MPa | ASTM 790 | |
| IZOD缺口冲击强度 | 8 | Kg.cm/cm | ASTM D-256 |
| 拉伸屈服强度 | 11400 | psi | ASTM D-638 |
| 弯曲强度 | 118 | MPa | ASTM D-790 |
| 弯曲模量 | 710 | psi | ASTM D-790 |
| 拉伸屈服强度 | 800 | Kg./cm | ASTM D-638 |
| 弯曲强度 | ASTM D-790 | ||
| 1200 | Kg/cm | ||
| 17000 | psi | ||
| IZOD缺口冲击强度 | 80 | J/m | ASTM D-256 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热变形温度 (1.82Mpa) | 157 | ℃ | ASTM D-648 |
| 耐燃性 | HB | class | ASTM D-UL94 |
| 热变形温度 (1.82Mpa) | 315 | °F | ASTM D-648 |