| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 成型收缩率 | 0.2-0.6 | % | ASTM D-955 |
| 熔体流动速率 | ASTM D-1238 | ||
| (220℃ 10kg) | 25 | g/10min | |
| (200℃ 5kg) | 2.5 | g/10min | |
| 比重 | 1.07 | ASTM D-792 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 伸长率 | 6 | % | ASTM D-638 |
| 拉伸强度 | 750 | kg/cm | ASTM D-638 |
| 弯曲弹性率 | 1300 | kg/cm | ASTM D-790 |
| 弯曲模量 | 36000 | kg/cm | ASTM D-790 |
| 洛氏硬度 | 123 | R | ASTM D-785 |
| IZOD冲击强度 | ASTM D-256 | ||
| (1/4" Notched) | 1.5 | kg.cm/cm | |
| (1/8" Notched) | 2.0 | kg.cm/cm |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| CTI | 1 | PLCCode | UL746A |
| HWI | 3 | PLCCode | UL746A |
| 抗弧光 | 5 | PLCCode | ASTM D-495 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热变形温度 (未退火 18.5kg/cm1/2") | 90 | ℃ | ASTM D-648 |
| 维卡软化点 (1000g) | 110 | ℃ | ASTM D-1525 |
| 燃烧性 | |||
| (1/8") | HB | UL-94 | |
| (1/8") | FH3-25 | mm/min | IEC707 |
| (1/16") | HB | UL-94 |