d.a.m.cond.Rheological properties
Molding shrinkage, parallel150x105x3; 270 °C / WZ 80 °C; 500bar%acc. ISO 25771.02
Molding shrinkage, transverse150x105x3; 270 °C / WZ 80 °C; 500bar%acc. ISO 25771.16
Post- shrinkage, parallel150x105x3; 120 °C; 4 h%acc. ISO25770.32
Post- shrinkage, transverse150x105x3; 120 °C; 4 h%acc. ISO25770.4
Mechanical properties (23 °C/50 % r. h.)CTensile modulus1mm/minMPaISO 527-1,-232001000CYield stress50 mm/minMPaISO527-1,-28040CYield strain50 mm/min%ISO 527-1,-24.020CNominal strainat break50 mm/min%ISO 527-1,-220> 50CTensile creep modulus1hMPaISO 899-1
800CTensile creep modulus1000 hMPaISO 899-1
600CCharpy impact strength23 °CkJ/m²ISO 179-1eUNNCCharpy impactstrength-30 °CkJ/m²ISO 179-1eUNNCCharpy notched impact strength23°CkJ/m²ISO 179-1eA< 1020CCharpy notched impact strength-30°CkJ/m²ISO 179-1eA<10<10
Izod impact strength23 °CkJ/m²ISO 180-1UNN
Izod impact strength-30 °CkJ/m²ISO 180-1UNN
Izod notched impact strength23 °CkJ/m²ISO 180-1A< 1030
Flexural modulus2 mm/minMPaISO 178-A2900850
Flexural strength2 mm/minMPaISO 178-A11035
Flexural strain at flexural strength2 mm/min%ISO 178-A6.08.0
Flexural stress at 3.5 % strain2 mm/minMPaISO 178-A9525CPuncturemaximum force23 °CNISO 6603-25900
CPuncture maximum force-30 °CNISO 6603-27300
CPuncture energy23 °CJISO 6603-290
CPuncture energy-30 °CJISO 6603-285
Ball indentation hardness
N/mm²ISO 2039-114050
Thermal propertiesCMelting temperature10 °C/min°CISO11357-1,-3222
CTemperature of deflection under load1.80 MPa°CISO 75-1,-255
CTemperature of deflection under load0.45 MPa°CISO 75-1,-2160
CTemperature of deflection under load8.00 MPa°CISO 75-1,-245
Vicat softening temperature50 N; 120 °C/h°CISO 306200
CCoefficient of linear thermal expansion, parallel23 to 55°C10-4/KISO 11359-1,-21.0
CCoefficient of linear thermal expansion, transverse23 to 55°C10-4/KISO 11359-1,-21.1
CBurning behavior UL 941.5 mmClassUL 94V-2
CBurning behavior UL 940.4 mmClassUL 94V-2
COxygen indexMethod A%ISO 4589-226
Glow wire test (GWFI)2.0 mm°CIEC 60695-2-12750
Burning behavior US-FMVSS302>=1.0 mm
ISO 3795passed
CVicat softening temperature50 N; 50 °C/h°CISO 306200
Electrical properties (23 °C/50 % r. h.)