牌号
LG
厂商
韩国LG
是否进口
进口
品名
ASA+PMMA
厂家(产地)
加工级别
注塑/挤出/模塑
特性级别
耐候户外用
用途级别
天线外壳 家具片材
销售方式
品牌经销
可售卖地
全国
货号
SG5009
ASAPMMA
Lupos? SG5009
Acrylonitrile Styrene Acrylate PMMA
Product Description:
Description General Purpose, Scratch Resistant ApplicationAutomotive Part (Radiator Grill, Side Mirror) ElectricElectronic(Housing, Components)
| General | |
Material Status | |
Literature1 | |
Search for UL Yellow Card | |
Availability | |
Features | |
Uses | |
Processing Method |
| Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | 1.15 | g/cm3 | ASTM D792 |
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow (23°C, 3.20 mm, Injection Molded) | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | ||
Tensile Strength2(Yield,23°C, 3.20 mm) | 49.0 | MPa | ASTM D638 |
Tensile Elongation2(Break,23°C, 3.20 mm, Injection Molded) | 20 | ASTM D638 | |
Flexural Modulus3(23°C,3.20 mm, Injection Molded) | 2060 | ASTM D790 | |
Flexural Strength3(23°C,3.20 mm, Injection Molded) | 68.6 | ASTM D790 | |
| Impact | Nominal Value | ||
Notched Izod Impact (23°C, 6.40 mm, Injection Molded) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | ||
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm,Injection Molded) | 80.0 | °C | ASTM D648 |
Vicat Softening Temperature | 92.0 | ASTM D15254 |
| Optical | Nominal Value | Test Method | |
Gloss | ASTM D2457 | ||
45° | 78 | ||
60° | 80 |
| Injection | Nominal Value | ||
Drying Temperature | 70 to 80 | ||
Drying Time | 3.0 to 4.0 | hr | |
Suggested Max Moisture | 0.020 | ||
Rear Temperature | 210 to 230 | ||
Middle Temperature | 220 to 250 | ||
Front Temperature | 240 to 260 | ||
Nozzle Temperature | 220 to 240 | ||
Processing (Melt) Temp | 220 to 260 | ||
Mold Temperature | 40 to 60 | ||
Back Pressure | 68.6 to 88.3 | ||
Screw Speed | rpm |
| Notes |
| 1These links provide you with access to supplier literature. Wework hard to keep them up to date; however you may find the mostcurrent literature from the supplier. |