PVDF 720 阿科玛 Arkema Kynar 720
Kynar®720
Polyvinylidene Fluoride
Arkema
产品说明：
KYNAR® 720 is a semi-crystalline low molecular weight pelletizedpolymer of vinylidene fluoride. It is a versatile engineeringplastic with an outstanding balance of physical and chemicalproperties which qualify it for high performance service in a widerange of applications. It is a thermoplastic fluoropolymer capableof being fabricated in standard processing equipment. The molecularweight and molecular weight distribution have been carefullytailored to supply a grade suitable for a variety of processingrequirements and end-use applications.
KYNAR® 720 is recommended for fine extrusion operations such asmonofilament and thin, flat, and blown film. It is also suitablefor injection molding applications where very thin cross-sectionsfor intricate design require excellent melt flow characteristics.KYNAR® 720 is also suggested for coextrusion of compositeconstructions and as a base for filled or alloyed KYNAR®compounds.
The powder form of this resin grade is available as KYNAR® 721PVDF.
物性信息：
| 基本信息 |
|
|---|
| 黄卡编号 | |
| 特性 | |
| 用途 | |
| 形式 | |
| 加工方法 | |
| 多点数据 | Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 1.77 到 1.79 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） | 5.0 到 27 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 肖氏硬度 (邵氏 D, 23°C) | 76 到 80 |
| ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 |
|
| ASTM D638 |
| 屈服, 23°C | 44.8 到 55.2 | MPa | ASTM D638 |
| 断裂, 23°C | 34.5 到 55.2 | MPa | ASTM D638 |
| 伸长率 (断裂, 23°C) | 20 到 100 | % | ASTM D638 |
| 弯曲模量 (23°C) | 1380 到 2310 | MPa | ASTM D790 |
| 弯曲强度 (23°C) | 58.6 到 75.8 | MPa | ASTM D790 |
| 压缩强度 (23°C) | 68.9 到 103 | MPa | ASTM D695 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 熔融峰值温度 | 165 到 172 | °C | ASTM D3418 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 体积电阻率 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|
| 熔体粘度 (232°C, 100 sec^-1) | 600 到 1200 | Pa·s | ASTM D3835 |