产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24小时 23℃ | ASTM D-570 | 1.3 | % |
| 比重 | ASTM D-792 | 1.25 | |||
| 物理性能 | 强化含量 | 15 | WT% | ||
| 抗燃级 | UL94 | HB | 1/16") | ||
| 泰伯磨耗量 | (1000g,CS-17)23℃ | ASTM D-1044 | 10 | mg/1000次 | |
| 机械性能 | 压缩强度 | 80℃ | ASTM D-695 | 700 | kg/cm2 |
| 抗拉屈股强度 | -40℃ | ASTM D-638 | 1400 | kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 51000 | kg/cm2 | |
| 埃佐德衡击 | 23℃ 无缺口1/8 | 30 | kg·cm/cm2 | ||
| 挠曲模量 | 80℃ | ASTM D-790 | 21000 | kg/cm2 | |
| 裂断伸长率 | 80℃ | ASTM D-638 | 9 | % | |
| 裂断伸长率 | -40℃ | ASTM D-638 | 3.5 | % | |
| 埃佐德衡击 | 23℃ V-缺口1/2 | ASTM D-256 | 5 | kg·cm/cm | |
| 挠曲强度 | 80℃ | ASTM D-790 | 700 | kg/cm2 | |
| 埃佐德衡击 | -40℃ V-缺口1/2 | ASTM D-256 | 4.5 | kg·cm/cm | |
| 洛氏硬度 | M-标度 23℃ | ASTM D-785 | 90 | ||
| 挠曲模量 | -40℃ | ASTM D-790 | 68000 | kg/cm2 | |
| 压缩强度 | -40℃ | ASTM D-695 | 2050 | kg/cm2 | |
| 埃佐德衡击 | -40℃ 无缺口1/8 | 19 | kg·cm/cm2 | ||
| 抗拉屈股强度 | 23℃ | ASTM D-638 | 1050 | kg/cm2 | |
| 抗拉屈股强度 | 80℃ | ASTM D-638 | 450 | kg/cm2 | |
| 裂断伸长率 | 23℃ | ASTM D-638 | 4 | % | |
| 洛氏硬度 | R-标度 23℃ | ASTM D-785 | 119 | ||
| 挠曲强度 | -40℃ | ASTM D-790 | 1800 | kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1500 | kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 1400 | kg/cm2 | |
| 电气性能 | 体积电阻率 | ASTM D-257 | 1015 | Ω·cm | |
| 介电强度 | 短时间 1/8" | ASTM D-149 | 20 | KV/mm | |
| 热性能 | 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 175 | ℃ |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 210 | ℃ | |
| 线性热膨胀系数 | ASTM D-696 | 4.5 | ×10-5cm/cm/℃ | ||
| 熔点 | 差示扫描测热计DSC | 225 | ℃ | ||
| 比热 | 0.37 | Cal/g·℃ | |||