产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 硬度 | ASTM D-785 | M-95 | ||
| 假密度 | ASTM D-1182 | 0.77 | g/cm3 | ||
| 吸水率 | ASTM D-570 | 0.3 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.19 | ||
| 全光透过率 | ASTM D-1003 | 92 | % | ||
| 流动系数 | ASTM D-1238 | 1.8 | g/10min | ||
| 燃烧率 | 1/16"HB | UL-94 | |||
| 成型收缩率 | ASTM D-955 | 0.002-0.006 | mm/mm | ||
| 机械性能 | 抗冲击力 | ASTM D-256 | 2.0 | kg-cm/cm | |
| 引张强度 | ASTM D-638/PSI | 10200/720 | Kg/cm2 | ||
| 弯曲强度 | ASTM D-790/PSI | 15600/1100 | Kg/cm2 | ||
| 延伸率 | ASTM D-638 | 5.0 | % | ||
| 曲折率 | ASTM D-542 | 1.491 | |||
| 绝缘耐力 | ASTM D-149 | 500 | Volts/Mil | ||
| 抗冲击力 | ASTM D-256 | 0.37 | ft-lbs/in2 | ||
| 电气性能 | 体积固有抵抗 | ASTM D-257 | 1015 | Ω.m | |
| 失电率 | ASTM D-150 | 0.19 | |||
| 诱电率 | ASTM D-150-647b | 3.7 | |||
| 诱电率力 | ASTM D-150-647 | 0.5 | |||
| 热性能 | 热变形温度 | ASTM D-648 | 100/212 | °C/°F | |
| 维卡软化点 | ASTM D-648 | 113/235 | °C/°F | ||
PMMA为无色透明的玻璃状物。是目前优良的高分子透明材料，可见光透过率达到92%，比玻璃的透光度高。热变性温度介于74°C~105°C间，密度1.14—1.20g/cc，成型收缩率0.2—0.8%。
PMMA具有质轻、价廉，易於成型等优点，溶于有机溶剂，如苯酚，苯甲醚等，通过旋涂可以形成良好的薄膜，具有良好的介电性能，可以作为有机场效应管（OFET）亦称有机薄膜晶体管（OTFT）的介质层。
PMMA制品在储存和使用过程中易出现银纹，银纹是材料中内应力造成的，因此在成型时应注意减少或避，也就是在成型时要有足够的保温时间