SABIC Innovative Plastics Cycoloy? CX5640 PC+ABS
Polymer,Thermoplastic,ABS Polymer,Polycarbonate/ABS Alloy,Unreinforced,Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明:
Cycoloy* CX5640 is a all purpose PC+ABS blend specially developedfor applications requiring weld line strength. High heat resistancecombined with good flow, excellent impact and low temperatureductility makes it a good candidate for various applications.
SABIC Innovative Plastics Cycoloy? CX5640 PC+ABS 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| 密度 | 1.15 g/cc | 0.0415 lb/in3 | ISO 1183 |
| 水分吸收 | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.40 % | 0.40 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 19 g/10 min @Load 5.00 kg, Temperature 260 °C | 19 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| 化合物熔体指数 | 18 g/10 min @Load 5.00 kg, Temperature 260 °C | 18 g/10 min @Load 11.0 lb, Temperature 500 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | >= 50 % | >= 50 % | Type I, 50 mm/min; ASTM D638 |
| >= 50 % | >= 50 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.40 GPa | 348 ksi | 5 mm/min; ASTM D638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 85.0 MPa | 12300 psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 1.50 J/cm | 2.81 ft-lb/in | Izod Impact, double-gated, 23°C; SABIC Method |
| 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 | |
| 3.00 J/cm @Temperature -30.0 °C | 5.62 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 50.0 kJ/m2 | 23.8 ft-lb/in2 | 80*10*3; ISO 180/1A | |
| 20.0 kJ/m2 @Temperature -30.0 °C | 9.52 ft-lb/in2 @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| 简支梁缺口冲击强度 | 5.00 J/cm2 | 23.8 ft-lb/in2 | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 2.00 J/cm2 @Temperature -30.0 °C | Edgew 80*10*3 sp=62mm; ISO 179/1eA | ||
| 落锤总能量 | 65.0 J @Temperature 23.0 °C | 47.9 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 70.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 70.0 μm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
| 线性热膨胀系数,横向流动 | 70.0 μm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | 122 °C @Thickness 3.20 mm | 252 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 108 °C @Thickness 3.20 mm | 226 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 130 °C | 266 °F | Rate B/50; ASTM D1525 |
| 130 °C | 266 °F | Rate B/50; ISO 306 | |
| 132 °C |