ASA粒
| 项目 Property | 单位 Unit | 试验方法 Test Method | 试验条件 Test Condition | ASA粒 | ||||
| 耐热 | 高流动 | 半透明 | 耐候 | 耐候 | ||||
| WE8100 | WE8100AF | WE810P | WG1700 | WF3300 | ||||
| 抗张強度 Tensile Strength | kg/cm2 (MPa) | ASTM D-638 (ISO527) | 23ºC | 470(46) | 420(41) | 400(39) | 440(43) | 480(47) |
| 弯曲強度 Flexural Strength | kg/cm2 (MPa) | ASTM D-790 (ISO178) | 23ºC | 760(75) | 740(73) | 660(65) | 780(77) | 800(79) |
| 弯曲模数 Flexural Modulus | kg/cm2 (MPa) | ASTM D-790 (ISO178) | 23ºC | 24000(2350) | 24000(2350) | 21000(2060) | 28000(2750) | 30000(2950) |
| 洛式硬度 Rockwell Hardness | R-Scale | ASTM D-785 (ISO2039/2) | 23ºC | R-103 | R-100 | R-100 | R-103 | R-100 |
| Izod冲击強度 Izod Impact Strength | kg-cm/cm (J/m) | ASTM D-256 (ISO R180) | 23ºC 1/4" bar | 20(196) | 16(157) | 16(157) | 14(137) | 20(196) |
| 卫氏软化点 VicatSoftening Temperature | ºC | ASTM D-1525 (ISO 306) | 1Kg load | / | / | / | 107 | 105 |
| 热变形温度 Heat Deflection Temperature | ºC | ASTM D-648 (ISO 75/A) | Unannealed 18.6kg/cm2 (1/2" bar) | 91 | 90 | 84 | 92 | 90 |
| 熔融指数 Melt Flow Index | g/10 min | ASTM D-1238 (ISO1133) | 220ºCx10Kg (98N) | 11 | 22 | 8 | 16 | 26 |
| 比重 Specific Gravity | g/cm2 | ASTM D-792 (ISO1183) | 23ºC/23ºC | 1.05 | 1.05 | 1.08 | 1.05 | 1.05 |
| 收缩率 Molding Shrinkage | % | ASTM D-995 | 3.2mm | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | / | / |
| 燃烧性 Flammability | / | UL-94 | FILE NO. E162823 | 1.5mm HB All Color | 1.5mm HB All Color | 1.5mm HB All Color | 1.5mm HB All Color | 1.5mm HB All Color |
| 特性 | 高耐候 高耐热 | 高耐候 高耐热 高流动 | 高耐候 透明 易著色 | 高耐候 颜色稳定性佳 | 高耐候 颜色稳定性佳 | |||