| 颜色 | - | |||
| ISO(JIS)材质表示 | ISO11469 (JIS K6999) | >COC< | ||
| 密度 | Kg/m³ | ISO1183 | 1,010 | |
| 吸水率 (23℃,饱和) | % | ISO 62 | 0.01 | |
| MVR (190℃,2.16kg) | cm³/10min | ISO1133 | 2.0 | |
| MVR (230℃,2.16kg) | cm³/10min | ISO1133 | 12.0 | |
| 玻璃化转变温度(10℃/min) | ℃ | ISO11357-1,-2,-3 | 78 | |
| 拉伸弹性模量(Film) (machine direction) | MPa | ISO527-3 | 2,100 | |
| 拉伸弹性模量(Film) (transverse direction) | MPa | ISO527-3 | 1,700 | |
| 拉伸破坏强度(Film) (machine direction) | MPa | ISO527-3 | 55 | |
| 拉伸破坏强度(Film) (transverse direction) | MPa | ISO527-3 | 50 | |
| 拉伸破坏伸率(Film) (machine direction) | % | ISO527-3 | 3.4 | |
| 引張破断伸度(Film) (transverse direction) | % | ISO527-3 | 3.4 | |
| 水蒸气透过性(Film) (38℃, 90%RH) | g?100μm/(m²?day) | ISO15106-3 | 0.85 | |
| 阻燃性 | UL94 | |||