性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 密度 | ASTM D-792 | 0.919 | g/m3 | |
熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.9 | g/10min | |
薄膜厚度 | 50.8 | um | |||
机械性能 | 割线模量 | 2% Secant,50.8um | ASTM D-882 | ||
MD | TD | ||||
168 | 238 | ||||
MPa | ||
拉伸屈服强度 | 50.8um | ASTM D-882 |
MD | TD | |
14.2 | 14.6 |
MPa | ||
拉伸断裂强度 | 50.8um | ASTM D-882 |
TD | MD | |
39.2 | 48.8 |
MPa | ||
拉伸断裂伸长率 | 50.8um | ASTM D-882 |
TD | MD | |
740 | 620 |
% | ||||
落锤冲击 | 50.8um | ASTM D-1709A | 300 | g |
埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 | ||
TD | MD | |||
1000 | 720 |
g | |||||
热性能 | 维卡软化点 | ASTM D-1525 | 107 | ℃ | |
熔融温度 | Internal Method | 120 | ℃ | ||
其它性能 | 电影穿刺抵抗 | 50.8um | Internal Method | 16.6 | J/cm3 |
光学性能 | 光泽度 | 45°,50.8um | ASTM D-2457 | 63 | |
雾度 | 50.8um | ASTM D-1003 | 12 | % |