Density / Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 23 | cm³/10min | ISO 1133 |
Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
Outdoor Suitability | f1 | UL 746C | |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/2C |
Notched Izod Impact | |||
-30°C | 100 | J/m | ASTM D256 |
23°C | 290 | J/m | ASTM D256 |
23°C 8 | 20 | kJ/m² | ISO 180/1A |
Unnotched Izod Impact (23°C) | 720 | J/m | ASTM D4812 |
Instrumented Dart Impact (23°C, Total Energy) | 50.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | 95.0 | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed, 3.20 mm | 78.0 | °C | ASTM D648 |
1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | 82.0 | °C | ISO 75-2/Af |