280°C/5.0 kg11 cm³/10 minISO 1133熔体质量流动速率(MFR)
280°C/5.0 kg12 g/10 minASTM D 1238收缩率
纵向(Flow)1.3~1.6 %Internalflow, 3.2 mm纵向(Flow)1.5~1.9 %InternalonTensile Bar, flow横向(Across Flow)1.1~1.4 %Internalxflow, 3.2mm吸水率3.5 %ISO 6223°C/sat吸湿率1.2 %ISO 6223°C / 50% RH磨耗15mg/1000cyInternalCS-17, 1 kg机械性能值/单位测试标准测试条件拉伸强度
屈服(yld)55 MpaASTM D638Type I, 50 mm/min屈服(yld)55 MpaISO 52750mm/min断裂(brk)55 MpaISO 52750 mm/min断裂(brk)55 MpaASTM D638Type I, 50mm/min拉伸延伸率
屈服(yld)15 %ASTM D638Type I, 50 mm/min屈服(yld)7.5 %ISO 52750mm/min断裂(brk)100 %ASTM D638Type I, 50 mm/min断裂(brk)60 %ISO 52750mm/min弯曲强度
屈服(yld)80 MpaASTM D7901.3 mm/min, 50 mm span屈服(yld)80 MpaISO 1782mm/min弯曲模量1900 MpaASTM D7901.3 mm/min, 50 mm span弯曲模量2000 MpaISO1782 mm/min拉伸模量1950 MpaASTM D63850 mm/min拉伸模量2100 MpaISO 5271mm/min冲击性能值/单位测试标准测试条件简支梁缺口(Charpy Notched)
-30℃ (-22℉)15 kJ/m²ISO 179/1eAV-notch Edgew 80*10*4 sp=62mm23℃(73℉)30 kJ/m²ISO 179/1eAV-notch Edgew 80*10*4 sp=62mm23℃ (73℉)30kJ/m²ISO 179/2C悬臂梁缺口(Izod Notched)
-30℃ (-22℉)120 J/mASTM D256-30℃ (-22℉)15 kJ/m²ISO 180/1A80*10*423℃(73℉)280 J/mASTM D25623℃ (73℉)30 kJ/m²ISO180/1A80*10*4仪器化落镖冲击能量
23℃ (73℉)总能量60 JASTM D3763硬度性能值/单位测试标准测试条件球压硬度90 MpaISO2039-1H358/30热学性能值/单位测试标准测试条件热变形温度(HDT)
0.45 Mpa (66 psi)（4.6kg/cm²）180 °CASTM D6483.2mm, unannealed0.45Mpa (66 psi)（4.6kg/cm²）180 °CISO 75/BeEdgew 120*10*4sp=100mm维卡软化温度(Vicat)195 °CASTM D1525Rate B/50维卡软化温度(Vicat)245°CISO 306Rate A/50维卡软化温度(Vicat)195 °CISO 306RateB/120维卡软化温度(Vicat)190 °CISO 306Rate B/50线性膨胀系数(CLTE)
纵向(Flow)90 E-6/°CASTM E831-40°C to 40°C, flow纵向(Flow)90 E-6/°CISO11359-223°C to 60°C, flow横向(Across Flow)95 E-6/°CASTM E831-40°C to40°C, xflow横向(Across Flow)90 E-6/°CISO 11359-223°C to 60°C,xflow导热系数0.23 W/m-°CISO 8302球压痕温度125 °CIEC60695-10-2PASS燃烧性能值/单位测试标准测试条件UL 防火等级
HB1.6 mmUL94
特性：高抗冲耐磨耐高温高强度抗化学优良的抗冲击性能及耐稳定性能耐温性化学性能和可加工性.
应用领域：电动工具
聚苯醚PPO塑料的优缺点
在温度升髙时，它的蠕变値增加也不大。抗冲击値在-60 9 1+65摄氏度的范围内是一常数，儿乎不受温度的影响。
耐热性好，熔点>300摄氏度,在高温下也能保持共强度和尺寸稳定性，热变形温度<18.5公斤/平方厘米）为1759 1180摄氏度,连续使用温度可达120摄氏度,