| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hrs | ASTM D-570 | 0.06 | % |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.06 | --- |
| 模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | 10-3 | |
| 阻燃性 | --- | UL94 | HB | --- | |
| 阻燃性 | --- | UL94 | 1.5 | mm | |
| 机械性能 | 洛氏硬度 | --- | ASTM D-785 | 119 | --- |
| 拉伸强度屈伏点断裂点 | 3.2mm3.2mm | ASTM D-638ASTM D-638 | 5930 | MPaMPa | |
| 弯曲强度 | 6.4mm | ASTM D-790 | 90 | MPa | |
| 弯曲模量 | 6.4mm | ASTM D-790 | 2418 | MPa | |
| 缺口冲击强度 | 23°C | ASTM D-256 | 213 | J/M | |
| 缺口冲击强度 | -40°C | ASTM D-256 | 133 | J/M | |
| 电气性能 | 损耗因数 | 60Hz | ASTM D-150 | 0.0004 | --- |
| 介电常数 | 60Hz | ASTM D-150 | 2.65 | --- | |
| 热 性 能 | UL长期使用温度电气含冲击无冲击 | --- | UL 746BUL 746BUL 746B | 10590105 | °C°C°C |
| 热变形强度 | 0.45MPa | ASTM D-648 | 137 | °C | |
| 热变形温度 | 1.8MPa | ASTM D-648 | 126 | °C | |
| 线膨胀系数 | --- | ASTM E-831 | 7.2×10-5 | 1/°C | |