Electrical Properties Metric English CommentsThermal PropertiesMetric English Comments
Volume Resistivity >=1.00e+13ohm-cm>=1.00e+13ohm-cmIEC60093
1.00e+16ohm-cm1.00e+16ohm-cmASTM D257
Surface Resistance >=1.00e+15ohm>=1.00e+15ohmIEC 60093
Dielectric Constant3.80
@Frequency 1000 Hz3.80
@Frequency 1000 HzASTM D150
3.80
@Frequency 1.00e+6 Hz3.80
@Frequency 1.00e+6 HzASTM D150
4.70
@Frequency 10000 Hz4.70
@Frequency 10000 HzIEC 60250
4.70
@Frequency 1.00e+6 Hz4.70
@Frequency 1.00e+6 HzIEC 60250
Dielectric Strength 27.0kV/mm686kV/inIEC 60243-1
Dissipation Factor0.000800
@Frequency 1000 Hz0.000800
@Frequency 1000 HzIEC 60250
0.000800
@Frequency 1.00e+6 Hz0.000800
@Frequency 1.00e+6 HzASTM D150
0.00100
@Frequency 1000 Hz0.00100
@Frequency 1000 HzASTM D150
0.00200
@Frequency 1.00e+6 Hz0.00200
@Frequency 1.00e+6 HzIEC 60250
Arc Resistance 156sec156secASTM D495
Comparative Tracking Index 150V150VIEC 60112
CTE, linear, Parallel to Flow 24.0µm/m-°C13.3µin/in-°FISO11359-2
CTE, linear, Transverse to Flow 32.0µm/m-°C17.8µin/in-°FISO11359-2
Specific Heat Capacity 1.50J/g-°C0.359BTU/lb-°F
Melting Point 280°C536°FISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 280°C536°FASTMD648
Deflection Temperature at 1.8 MPa (264 psi) 265°C509°FASTMD648
270°C518°FISO 75-1, -2
Deflection Temperature at 8.0 MPa 215°C419°FISO 75-1, -2
Glass Transition Temp, Tg 90.0°C194°FISO 11357-1,-2,-3
Flammability, UL94V-0
@Thickness 0.750 mmV-0
@Thickness 0.0295 in
V-0
@Thickness 1.50 mmV-0
@Thickness 0.0591 in