PC 上海科思创（拜耳） 9415 000000
高强度防火PC 加纤增强 GF10德国拜耳9415
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 | 脱模性能粘度，高阻燃性 |
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| 灼热丝易燃指数 | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| 热灯丝点火温度 | IEC 60695-2-13 | ||
| 0.750 mm | 900 | °C | |
| 1.50 mm | 900 | °C | |
| 3.00 mm | 900 | °C | |
| 氧指数 10 | 35 | % | ISO 4589-2 |
| Application of Flame fromSmall Burner | |||
| 2.00mm 11 | K1, F1 | DIN 53438-1, -3 | |
| 2.00 mm | B2 | DIN 4102 | |
| Burning Rate 12 (> 1.00mm) | Passed | ISO 3795 | |
| Flash IgnitionTemperature | 470 | °C | ASTM D1929 |
| Needle FlameTest | IEC 60695-11-5 | ||
| Method F : 1.50 mm | 2.0 | min | |
| Method F : 2.00 mm | 2.0 | min | |
| Method F : 3.00 mm | 2.0 | min | |
| Method K : 1.50 mm | 1.0 | min | |
| Method K : 2.00 mm | 2.0 | min | |
| Method K : 3.00 mm | 2.0 | min | |
| Self IgnitionTemperature | 550 | °C | ASTM D1929 |
工程塑料：
ASA PA6 PA66 PBT PC PC/ABS PCTAPCTG PETG POM AES COC CPVC LCP PA12 PA46 PA612
PA6T PA9T PCT PEEK PEI PESPPA PPE PPO PPS PTFE SMMA
聚碳酸酯是一种强韧的热塑性树脂，其名称来源于其内部的CO3基团。可由双酚A和氧氯化碳（COCl2）合成。现较多使用的方法为熔融酯交换法（双酚A和碳酸二苯酯通过酯交换和缩聚反应合成）。
聚碳酸酯耐弱酸，耐弱碱，耐中性油。
聚碳酸酯不耐紫外光，不耐强碱。
PC是一种线型碳酸聚酯，分子中碳酸基团与另一些基团交替排列，这些基团可以是芳香族，可以是脂肪族，也可两者皆有。双酚A型PC是重要的工业产品。
PC是几乎无色的玻璃态的无定形聚合物，有很好的光学性。PC高分子量树脂有很高的韧性，悬臂梁缺口冲击强度为600~900J/m，未填充牌号的热变形温度大约为130°C，玻璃纤维增强后可使这个数值增加10°C。PC的弯曲模量可达2400MPa以上，树脂可加工制成大的刚性制品。低于100°C时，在负载下的蠕变率很低。PC耐水解性差，不能用于重复经受高压蒸汽的制品。
PC主要性能缺陷是耐水解稳定性不够高，对缺口敏感，耐有机化学品性，耐刮痕性较差，长期暴露于紫外线中会发黄。和其他树脂一样，PC容易受某些有机溶剂的侵蚀。
PC材料具有阻燃性，耐磨。抗氧化性。
聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比，聚碳酸酯的耐冲击性能好，折射率高，加工性能好，不需要添加剂就具有UL94V-0级阻燃性能。但是聚甲基丙烯酸甲酯相对聚碳酸酯价格较低，并可通过本体聚合的方法生产大型的器件。
聚碳酸酯的耐磨性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理。