供应590R-RS酸洗卷590R-RS宝钢

Q/BQB 310－2018 4 表 2 型号 成分 a（摩尔质量） ％ C Si Mn P S Alt SAPH310≤0.10 ≤0.30 ≤0.80 ≤0.025 ≤0.020 ≥0.010 SAPH370 ≤0.21 ≤0.30 ≤1.00SAPH400 ≤0.21 ≤0.30 ≤1.40 ≤0.025 ≤0.020 SAPH440 ≤1.60 SPFH540 ≤0.15≤0.50 ≤1.80 SPFH590 ≤0.18 ≤0.60 ≤2.00 ≤0.025 ≤0.020 SPFH780 ≤0.20≤1.00 ≤2.10 B440QK ≤0.21 ≤0.35 ≤1.80 ≤0.025 ≤0.020 B330CL ≤0.10≤0.30 ≤0.80 B380CL ≤0.12 ≤0.30 ≤1.50 ≤0.025 ≤0.020 B420CL ≤0.12≤0.30 ≤1.50 B450CL ≤0.10 ≤0.30 ≤1.50 ≤0.025 ≤0.020 B500CL ≤0.12≤0.30 ≤1.60 ≤0.025 ≤0.020 B530CL ≤0.12 ≤0.30 ≤1.60 ≤0.025 ≤0.020B550CL ≤0.12 ≤0.30 ≤2.00 ≤0.025 ≤0.020 B600CL ≤0.15 ≤0.30 ≤2.00≤0.025 ≤0.020 B650CL ≤0.15 ≤0.50 ≤2.00 ≤0.025 ≤0.020 B320L ≤0.10≤0.30 ≤0.80 ≤0.025 ≤0.020 B420L ≤0.12 ≤0.50 ≤1.50 ≤0.020 B510L≤0.16 ≤0.50 ≤1.60 ≤0.020 B510DL ≤0.18 ≤0.30 ≤1.60 ≤0.025 ≤0.020B550L ≤0.16 ≤0.50 ≤1.60 ≤0.025 ≤0.020 B440QZR ≤0.12 ≤0.50 ≤1.30≤0.025 ≤0.020 － B480QZR ≤0.16 ≤0.50 ≤1.50 ≤0.020 a为改进钢的特性，依据必须可加上别的铝合金原素，这时 Alt 的低限不规定。 表 3 型号 成分 a（摩尔质量） ％ C Si Mn PS Alt 别的 QStE340TM ≤0.12 ≤0.50 ≤1.30 ≤0.025 ≤0.020 ≥0.015 Nb≤0.09V≤0.20 Ti≤0.15 QStE380TM ≤1.40 QStE420TM ≤1.50 QStE460TM ≤1.60QStE500TM ≤1.70 a 为改进钢的特性，依据必须可加上 Nb、V、Ti 中一种或几类铝合金原素，但 Nb VTi≤0.22%。 Q/BQB 310－2018 5 表 4 型号 成分 a （摩尔质量） ％ C Mn Si P S Alt NbaV a Tia Mo B QStE550TM B610L(B600L) ≤0.12 ≤1.80 ≤0.50 ≤0.025 ≤0.015≥0.015 ≤0.09 ≤0.20 ≤0.15 － － QStE600TM B650L ≤0.12 ≤1.90 ≤0.50≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.22 ≤0.50 ≤0.005 QStE650TM B700L≤0.12 ≤2.00 ≤0.60 ≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.22 ≤0.50≤0.005 QStE700TM B750L ≤0.12 ≤2.10 ≤0.60 ≤0.025 ≤0.015 ≥0.015 ≤0.09≤0.20 ≤0.22 ≤0.50 ≤0.005 a 钢中可加上 Nb、V、Ti 中一种或几类铝合金原素，但 Nb VTi≤0.22。 6.5 结构力学和使用性能 6.5.1 厚钢板及钢链的结构力学和使用性能应合乎相对表 5～表 10 的要求。6.5.2 弯折实验后，试件的外表层不可有人眼的裂痕。供货方如能确保弯折实验达标，