供应沙伯基础1103 耐低温抗撞击PC/PBT
供应沙伯基础1103 耐低温抗撞击PC/PBT
XENOY™ 1103 resin 物性表
基本信息黄卡编号E121562-100149124添加剂冲击改性剂特性冲击改性耐低温冲击耐化学性良好用途汽车领域的应用外观黑色灰色加工方法注射成型多点数据Coefficientof Thermal Expansion vs. Temperature (ASTM E831)Compressive Stressvs. Strain (ASTM D695)Flexural DMA (ASTMD4065)Pressure-Volume-Temperature (PVT - Zoller Method)Shear DMA(ASTM D4065)Specific Heat vs. Temperature (ASTM D3417)Tensile Creep(ASTM D2990)Tensile FatigueTensile Stress vs. Strain (ASTMD638)Thermal Conductivity vs. Temperature (ASTM E1530)Viscosity vs.Shear Rate (ASTM D3835)物理性能额定值单位制测试方法比重1.20g/cm³ASTMD792熔流率（熔体流动速率） (250°C/5.0kg)13g/10 minASTM D1238收缩率 - 流动 (3.20 mm)0.80 到1.0%内部方法机械性能额定值单位制测试方法拉伸模量 11900MPaASTMD638抗张强度 2ASTMD638 屈服51.7MPaASTMD638 断裂50.3MPaASTM D638伸长率 3ASTMD638 屈服5.0%ASTMD638 断裂150%ASTMD638弯曲模量 4(50.0 mm跨距)1930MPaASTM D790弯曲强度 5(屈服, 50.0 mm 跨距)77.2MPaASTMD790冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°C)750J/mASTM D256装有测量仪表的落镖冲击 (23°C, Total Energy)61.0JASTMD3763热性能额定值单位制测试方法载荷下热变形温度ASTMD648 0.45 MPa, 未退火,3.20 mm104°CASTM D648 1.8 MPa, 未退火, 3.20 mm87.8°CASTMD648维卡软化温度126°CASTM D1525 6线形热膨胀系数ASTME831 流动 : -40 到40°C1.7E-4cm/cm/°CASTME831 横向 : -40 到40°C2.0E-4cm/cm/°CASTM E831注射额定值单位制干燥温度110°C干燥时间4.0 到6.0hr干燥时间，大8.0hr建议的大水分含量0.020%建议注射量50 到 80%料筒后部温度238 到260°C料筒中部温度243 到 266°C料筒前部温度249 到 271°C射嘴温度249 到 266°C加工（熔体）温度254 到277°C模具温度38 到 88°C背压0.345 到 0.689MPa螺杆转速40 到 80rpm排气孔深度0.013 到0.020mm