| 密度 | 干 | ASTMD-792 | 1.14 | |
| ASTMD792 | 1.14 | g/cm³ | ||
| 收缩率 | MD2.0mm | ASTMD995 | 1.3 | % |
| TD2.0mm | ASTMD995 | 2.0 | % | |
| 干 | 旭化成方法 | 1.3-2.0 | % | |
| 吸水率 | (23°C,24hr) | ASTMD570 | 2.5 | % |
| 断裂伸长率 | 23°C | ASTMD638 | 50 | % |
| ASTMD638/ISO 527 | 50 | % | ||
| 断裂延伸率 | 干(湿) | ASTMD-638 | 50(250) | % |
| 抗挠强度 | 干(湿) | ASTMD-790 | 118(54) | Mpa |
| 抗挠系数 | 干(湿) | ASTMD-790 | 2.8(1.2) | GPa |
| 拉伸强度 | 干(湿) | ASTMD-638 | 79(57) | Mpa |
| 23°C | ASTMD638 | 79 | Mpa | |
| 洛氏硬度 | 干(湿) | ASTMD-785 | 120(108) | Rscale |
| 干(湿) | ASTMD-785 | 80(55) | MScale | |
| 磨耗率 | 湿 | ASTMD-1044 | 7 | |
| 弯曲模量 | 23°C | ASTMD790 | 2800 | Mpa |
| ASTMD790/ISO 178 | 2790 | kg·cm/cm(J/M)ft·lb/in | ||
| 弯曲强度 | ASTMD790/ISO 178 | 118 | kg·cm/cm(J/M)ft·lb/in | |
| 23°C | ASTMD790 | 118 | Mpa | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 39 | J/m |
| 悬臂梁式缺口冲击强度 | 干(湿) | ASTMD-256 | 39(147) | J/m |
| Charpy冲击强度 | ASTMD256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in | |
| 比热容 | 干 | 1670 | J/(kg.k) | |
| 导热率 | 干 | 0.2 | W/(m.K) | |
| 燃烧性（率） | UL94 | v-2 | ||
| 热变形温度 | ASTMD648/ISO 75 | 230 | ℃（℉） | |
| 0.46MPa,干 | ASTMD-648 | 230 | ℃ | |
| 1.82MPa,干 | ASTMD-648 | 70 | ℃ | |
| 0.45MPa未退火 | ASTMD648 | 230 | °C | |
| 1.80MPa未退火 | ASTMD648 | 70 | °C | |
| 线膨胀系数 | 导热系数 | JISR2618 | 0.2 | W/m/K |
| 比热 | 1670 | J/kg/°C | ||
| 线性膨胀系数 | 干 | ASTMD-696 | 8 | |
| ASTMD696/ISO 11359 | 8 | mm/mm.℃ | ||
| 阻燃性 | 干 | UL94 | V-2 | |
| 耗散因数 | 相对漏电起痕指数 | ASTMD3638 | 600 | V |
| 绝缘强度 | ASTMD149 | 20 | KV/mm | |
| 体积电阻率 | ASTMD257/IEC 60093 | 10-10 | Ω.cm | |
| 洛氏硬度 | ASTMD785 | 80 | M（Scale） | |
| ASTMD785 | 120 | R | ||
| 防火等级 | UL-94 | 0.40mm | V-2 | |
| UL-94 | 0.71mm | V-2 | ||
| UL-94 | 1.50mm | V-2 | ||
| UL-94 | 3.00mm | V-2 | ||
| 氧指数 | ASTM2863 | 26 | % | |
| 密度 | ASTMD792/ISO 1183 | 1.14 | ||
| 吸水率23℃/24H | ASTMD570/ISO 62 | 2.5 | % | |
| 吸湿率 | 湿 | 2.5 | % | |
| 氧指数 | 干 | ASTMD-2863 | 26 | % |